Certain Carbon and Alloy Steel Cut-to-Length Plate From the People's Republic of China: Antidumping Duty Order

AGENCY:

Enforcement and Compliance, International Trade Administration, Department of Commerce.

SUMMARY:

Based on affirmative final determinations by the Department of Commerce (the Department) and the International Trade Commission (ITC), the Department is issuing an antidumping duty order on Certain Carbon and Alloy Steel Cut-to-Length Plate (CTL plate) from the People's Republic of China (PRC).

DATES:

Effective March 20, 2017.

FOR FURTHER INFORMATION CONTACT:

Irene Gorelik, AD/CVD Operations, Office VIII, Enforcement and Compliance, International Trade Administration, U.S. Department of Commerce, 1401 Constitution Avenue NW., Washington, DC 20230; telephone: (202) 482-6905.

SUPPLEMENTARY INFORMATION:

Background

In accordance with section 735(d) and 777(i)(1) of the Tariff Act of 1930, as amended (the Act), and 19 CFR 351.210(c), on January 26, 2017, the Department published its affirmative final determination in the less than fair value (LTFV) investigation of CTL plate from the PRC. On March 13, 2017, the ITC notified the Department of its final determination pursuant to section 735(b)(1)(A)(i) of the Act, that an industry in the United States is materially injured or threatened with material injury by reason of imports of CTL plate from the PRC.

Scope of the Order

The products covered by this order are certain carbon and alloy steel hot-rolled or forged flat plate products not in coils, whether or not painted, varnished, or coated with plastics or other non-metallic substances (cut-to-length plate). Subject merchandise includes plate that is produced by being cut-to-length from coils or from other discrete length plate and plate that is rolled or forged into a discrete length. The products covered include (1) Universal mill plates (i.e., flat-rolled products rolled on four faces or in a closed box pass, of a width exceeding 150 mm but not exceeding 1250 mm, and of a thickness of not less than 4 mm, which are not in coils and without patterns in relief), and (2) hot-rolled or forged flat steel products of a thickness of 4.75 mm or more and of a width which exceeds 150 mm and measures at least twice the thickness, and which are not in coils, whether or not with patterns in relief. The covered products described above may be rectangular, square, circular or other shapes and include products of either rectangular or non-rectangular cross-section where such non-rectangular cross-section is achieved subsequent to the rolling process, i.e., products which have been “worked after rolling” (e.g., products which have been beveled or rounded at the edges). For purposes of the width and thickness requirements referenced above, the following rules apply:

(1) except where otherwise stated where the nominal and actual thickness or width measurements vary, a product from a given subject country is within the scope if application of either the nominal or actual measurement would place it within the scope based on the definitions set forth above unless the product is already covered by an order existing on that specific country (e.g., Notice of the Antidumping Duty Order: Certain Hot-Rolled Carbon Steel Flat Products From the People's Republic of China, 66 FR 59561 (November 29, 2001)); and

(2) where the width and thickness vary for a specific product (e.g., the thickness of certain products with non-rectangular cross-section, the width of certain products with non-rectangular shape, etc.), the measurement at its greatest width or thickness applies.

Steel products included in the scope of this order are products in which: (1) Iron predominates, by weight, over each of the other contained elements; and (2) the carbon content is 2 percent or less by weight.

Subject merchandise includes cut-to-length plate that has been further processed in the subject country or a third country, including but not limited to pickling, oiling, levelling, annealing, tempering, temper rolling, skin passing, painting, varnishing, trimming, cutting, punching, beveling, and/or slitting, or any other processing that would not otherwise remove the merchandise from the scope of the order if performed in the country of manufacture of the cut-to-length plate.

All products that meet the written physical description, are within the scope of this order unless specifically excluded or covered by the scope of an existing order. The following products are outside of, and/or specifically excluded from, the scope of this order:

(1) Products clad, plated, or coated with metal, whether or not painted, varnished or coated with plastic or other non-metallic substances;

(2) military grade armor plate certified to one of the following specifications or to a specification that references and incorporates one of the following specifications:

• MIL-A-12560,
• MIL-DTL-12560H,
• MIL-DTL-12560J,
• MIL-DTL-12560K,
• MIL-DTL-32332,
• MIL-A-46100D,
• MIL-DTL-46100-E,
• MIL-46177C,
• MIL-S-16216K Grade HY80,
• MIL-S-16216K Grade HY100,
• MIL-S-24645A HSLA-80;
• MIL-S-24645A HSLA-100,
• T9074-BD-GIB-010/0300 Grade HY80,
• T9074-BD-GIB-010/0300 Grade HY100,
• T9074-BD-GIB-010/0300 Grade HSLA80,
• T9074-BD-GIB-010/0300 Grade HSLA100, and
• T9074-BD-GIB-010/0300 Mod. Grade HSLA115,

except that any cut-to-length plate certified to one of the above specifications, or to a military grade armor specification that references and incorporates one of the above specifications, will not be excluded from the scope if it is also dual- or multiple-certified to any other non-armor specification that otherwise would fall within the scope of this order;

(3) stainless steel plate, containing 10.5 percent or more of chromium by weight and not more than 1.2 percent of carbon by weight;

(4) CTL plate meeting the requirements of ASTM A-829, Grade E 4340 that are over 305 mm in actual thickness;

(5) Alloy forged and rolled CTL plate greater than or equal to 152.4 mm in actual thickness meeting each of the following requirements:

(a) Electric furnace melted, ladle refined & vacuum degassed and having a chemical composition (expressed in weight percentages):

• Carbon 0.23-0.28,
• Silicon 0.05-0.20,
• Manganese 1.20-1.60,
• Nickel not greater than 1.0,
• Sulfur not greater than 0.007,
• Phosphorus not greater than 0.020,
• Chromium 1.0-2.5,
• Molybdenum 0.35-0.80,
• Boron 0.002-0.004,
• Oxygen not greater than 20 ppm,
• Hydrogen not greater than 2 ppm, and
• Nitrogen not greater than 60 ppm;

(b) With a Brinell hardness measured in all parts of the product including mid thickness falling within one of the following ranges:

(i) 270-300 HBW,

(ii) 290-320 HBW, or

(iii) 320-350 HBW;

(c) Having cleanliness in accordance with ASTM E45 method A (Thin and Heavy): A not exceeding 1.5, B not exceeding 1.0, C not exceeding 0.5, D not exceeding 1.5; and

(d) Conforming to ASTM A578-S9 ultrasonic testing requirements with acceptance criteria 2 mm flat bottom hole;

(6) Alloy forged and rolled steel CTL plate over 407 mm in actual thickness and meeting the following requirements:

(a) Made from Electric Arc Furnace melted, Ladle refined & vacuum degassed, alloy steel with the following chemical composition (expressed in weight percentages):

• Carbon 0.23-0.28,
• Silicon 0.05-0.15,
• Manganese 1.20-1.50,
• Nickel not greater than 0.4,
• Sulfur not greater than 0.010,
• Phosphorus not greater than 0.020,
• Chromium 1.20-1.50,
• Molybdenum 0.35-0.55,
• Boron 0.002-0.004,
• Oxygen not greater than 20 ppm,
• Hydrogen not greater than 2 ppm, and
• Nitrogen not greater than 60 ppm;

(b) Having cleanliness in accordance with ASTM E45 method A (Thin and Heavy): A not exceeding 1.5, B not exceeding 1.5, C not exceeding 1.0, D not exceeding 1.5;

(c) Having the following mechanical properties:

(i) With a Brinell hardness not more than 237 HBW measured in all parts of the product including mid thickness; and having a Yield Strength of 75ksi min and UTS 95ksi or more, Elongation of 18% or more and Reduction of area 35% or more; having charpy V at −75 degrees F in the longitudinal direction equal or greater than 15 ft. lbs (single value) and equal or greater than 20 ft. lbs (average of 3 specimens) and conforming to the requirements of NACE MR01-75; or

(ii) With a Brinell hardness not less than 240 HBW measured in all parts of the product including mid thickness; and having a Yield Strength of 90 ksi min and UTS 110 ksi or more, Elongation of 15% or more and Reduction of area 30% or more; having charpy V at −40 degrees F in the longitudinal direction equal or greater than 21 ft. lbs (single value) and equal or greater than 31 ft. lbs (average of 3 specimens);

(d) Conforming to ASTM A578-S9 ultrasonic testing requirements with acceptance criteria 3.2 mm flat bottom hole; and

(e) Conforming to magnetic particle inspection in accordance with AMS 2301;

(7) Alloy forged and rolled steel CTL plate over 407 mm in actual thickness and meeting the following requirements:

(a) Made from Electric Arc Furnace melted, ladle refined & vacuum degassed, alloy steel with the following chemical composition (expressed in weight percentages):

• Carbon 0.25-0.30,
• Silicon not greater than 0.25,
• Manganese not greater than 0.50,
• Nickel 3.0-3.5,
• Sulfur not greater than 0.010,
• Phosphorus not greater than 0.020,
• Chromium 1.0-1.5,
• Molybdenum 0.6-0.9,
• Vanadium 0.08 to 0.12
• Boron 0.002-0.004,
• Oxygen not greater than 20 ppm,
• Hydrogen not greater than 2 ppm, and
• Nitrogen not greater than 60 ppm.

(b) Having cleanliness in accordance with ASTM E45 method A (Thin and Heavy): A not exceeding 1.0(t) and 0.5(h), B not exceeding 1.5(t) and 1.0(h), C not exceeding 1.0(t) and 0.5(h), and D not exceeding 1.5(t) and 1.0(h);

(c) Having the following mechanical properties: A Brinell hardness not less than 350 HBW measured in all parts of the product including mid thickness; and having a Yield Strength of 145ksi or more and UTS 160ksi or more, Elongation of 15% or more and Reduction of area 35% or more; having charpy V at −40 degrees F in the transverse direction equal or greater than 20 ft. lbs (single value) and equal or greater than 25 ft. lbs (average of 3 specimens);

(d) Conforming to ASTM A578-S9 ultrasonic testing requirements with acceptance criteria 3.2 mm flat bottom hole; and

(e) Conforming to magnetic particle inspection in accordance with AMS 2301.

Excluded from the scope of the antidumping duty order on cut-to-length plate from the People's Republic of China are any products covered by the existing antidumping duty order on certain cut-to-length carbon steel plate from the People's Republic of China. See Suspension Agreement on Certain Cut-to-Length Carbon Steel Plate from the People's Republic of China; Termination of Suspension Agreement and Notice of Antidumping Duty Order, 68 FR 60,081 (Dep't Commerce Oct. 21, 2003), as amended, Affirmative Final Determination of Circumvention of the Antidumping Duty Order on Certain Cut-to-Length Carbon Steel Plate from the People's Republic of China, 76 FR 50,996, 50,996-97 (Dep't of Commerce Aug. 17, 2011). On August 17, 2011, the U.S. Department of Commerce found that the order covered all imports of certain cut-to-length carbon steel plate products with 0.0008 percent or more boron, by weight, from China not meeting all of the following requirements: aluminum level of 0.02 percent or greater, by weight; a ratio of 3.4 to 1 or greater, by weight, of titanium to nitrogen; and a hardenability test (i.e., Jominy test) result indicating a boron factor of 1.8 or greater.

The products subject to the order are currently classified in the Harmonized Tariff Schedule of the United States (HTSUS) under item numbers: 7208.40.3030, 7208.40.3060, 7208.51.0030, 7208.51.0045, 7208.51.0060, 7208.52.0000, 7211.13.0000, 7211.14.0030, 7211.14.0045, 7225.40.1110, 7225.40.1180, 7225.40.3005, 7225.40.3050, 7226.20.0000, and 7226.91.5000.

The products subject to the order may also enter under the following HTSUS item numbers: 7208.40.6060, 7208.53.0000, 7208.90.0000, 7210.70.3000, 7210.90.9000, 7211.19.1500, 7211.19.2000, 7211.19.4500, 7211.19.6000, 7211.19.7590, 7211.90.0000, 7212.40.1000, 7212.40.5000, 7212.50.0000, 7214.10.0000, 7214.30.0010, 7214.30.0080, 7214.91.0015, 7214.91.0060, 7214.91.0090, 7225.11.0000, 7225.19.0000, 7225.40.5110, 7225.40.5130, 7225.40.5160, 7225.40.7000, 7225.99.0010, 7225.99.0090, 7226.11.1000, 7226.11.9060, 7226.19.1000, 7226.19.9000, 7226.91.0500, 7226.91.1530, 7226.91.1560, 7226.91.2530, 7226.91.2560, 7226.91.7000, 7226.91.8000, and 7226.99.0180.

The HTSUS subheadings above are provided for convenience and customs purposes only. The written description of the scope of the order is dispositive.

Antidumping Duty Order

In accordance with sections 735(b)(1)(A)(i) and 735(d) of the Act, the ITC has notified the Department of its final determination in this investigation, in which it found that imports of CTL plate from the PRC are materially injuring or threatening material injury to a U.S. industry. Therefore, in accordance with section 735(c)(2) of the Act, we are publishing this antidumping duty order.

As a result of the ITC's final determination, in accordance with section 736(a)(1) of the Act, the Department will direct U.S. Customs and Border Protection (CBP) to assess, upon further instruction by the Department, antidumping duties equal to the amount by which the normal value of the merchandise exceeds the export price (or constructed export price) of the merchandise, for all relevant entries of CTL plate from the PRC. These antidumping duties will be assessed on unliquidated entries from the PRC entered, or withdrawn from warehouse, for consumption on or after November 14, 2016, the date on which the Department published the Preliminary Determination, but will not include entries occurring after the expiration of the provisional measures period and before publication of the ITC's final injury determination, as further described below.

Continuation of Suspension of Liquidation

In accordance with section 735(c)(1)(B) of the Act, we will instruct CBP to continue to suspend liquidation on entries of subject merchandise from the PRC. We will also instruct CBP to require cash deposits equal to the estimated amount by which the normal value exceeds the U.S. price as indicated in the chart below. These instructions suspending liquidation will remain in effect until further notice.

Accordingly, effective on the date of publication of the ITC's final affirmative injury determination, CBP will require, at the same time as importers would normally deposit estimated duties on this subject merchandise, a cash deposit equal to the estimated antidumping duty margin as discussed above. The “PRC-wide” rate applies to all exporters of subject merchandise not specifically listed.

Provisional Measures

Section 733(d) of the Act states that instructions issued pursuant to an affirmative preliminary determination may not remain in effect for more than four months except where exporters representing a significant proportion of exports of the subject merchandise request the Department to extend that four-month period to no more than six months. However, the Department did not extend the four-month period in the underlying investigation. In the underlying investigation, the Department published the Preliminary Determination on November 14, 2016. Thus, the four-month period beginning on the date of the publication of the Preliminary Determination ended on March 14, 2017. Furthermore, section 737(b) of the Act states that definitive duties are to begin on the date of publication of the ITC's final injury determination.

Therefore, in accordance with section 733(d) of the Act and our practice, we will instruct CBP to terminate the suspension of liquidation and to liquidate, without regard to antidumping duties, unliquidated entries of CTL plate from the PRC entered, or withdrawn from warehouse, for consumption after March 14, 2017, the date the provisional measures expired, and through the day preceding the date of publication of the ITC's final injury determination in the Federal Register.

Estimated Dumping Margin

The Department determines that the estimated final dumping margin is as follows:

Notification to Interested Parties

This notice constitutes the antidumping duty order with respect to CTL plate from the PRC, pursuant to section 736(a) of the Act. Interested parties may contact the Department's Central Records Unit, Room B8024 of the main Commerce building, for copies of an updated list of antidumping duty orders currently in effect.

This order is issued and published in accordance with sections 736(a) of the Act and 19 CFR 351.211(b).